The alloy AlCu6MnZrTi/ER 2319 is heat treatable and produces higher strength and ductility than the 4xxx series filler alloys when welds in 2014, 2036, 2219 and Al-Cu casting alloys are post welds heat-treated
CHEMICAL COMPOSITION
Al
remainder
Zr
0,10 - 0,25
Si
<0,20
Fe
<0,30
Cu
5,8 - 6,8
Mn
0,20 - 0,40
Mg
<0,02
Zn
<0,10
Ti
0,10 - 0,20
Be
<0,0003
V
0,05 - 0,15
Others each <0,05
Others tot. <0,15
TYPICAL AS-WELDED PROPERTIES
OF MIG AND TIG WELD JOINTS
BASE METAL
FILLER ALLOY
TENSILE STRENGTH
2219-T62
2319
248 N/mm2(1) or 344 N/mm2(2)
2219-T81
2319
262 N/mm2(1)
2219-T81
2319
282 N/mm2(1) or 296 N/mm2(2)
NOTE: (1) as welded (2) Post weld heat treated and aged
SHIELDING GASES
FOR GMAW / GTAW
Ar 99,99% min.
Ar 75% + He 25%
Ar 50% + He 50%
AVAILABLE SIZES
MIG: 6-7 Kg D300 or K300/KS300 Spools
WIRE DIAMETER
0,8 mm
1,0 mm
1,2 mm
1,6 mm
2,0 mm
2,4 mm
10 Kg TIG Carton box (length 1000 mm)
RODS
DIAMETER
1,6 mm
2,0 mm
2,4 mm
3,2 mm
4,0 mm
5,0 mm
MORE DIAMETERS AND PACKAGING UPON REQUEST